Product Description
S-Plastics Thermocomp TH0815A resin is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 18 | MPa | ASTM D 638 |
| Tensile Stress, break | 16 | MPa | ASTM D 638 |
| Tensile Strain, yield | 13.2 | % | ASTM D 638 |
| Tensile Strain, break | 25.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1330 | MPa | ASTM D 638 |
| Flexural Stress | 20 | MPa | ASTM D 790 |
| Flexural Modulus | 1520 | MPa | ASTM D 790 |
| Tensile Stress, yield | 19 | MPa | ISO 527 |
| Tensile Stress, break | 17 | MPa | ISO 527 |
| Tensile Strain, yield | 13.7 | % | ISO 527 |
| Tensile Strain, break | 26.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1120 | MPa | ISO 527 |
| Flexural Stress | 21 | MPa | ISO 178 |
| Flexural Modulus | 1390 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1057 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 144 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 16 | J | ASTM D 3763 |
| Multiaxial Impact | 12 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 73 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 42 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 8.77E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.25E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 44 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 8.15 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.5 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.48 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.49 | % | ISO 294 |
| Density | 8.15 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Source GMD, last updated:10/11/2005 |
Processing
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
| (2) Only typical data for selection purposes. Not to be used for part or tool design. |
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| (4) Internal measurements according to UL standards. |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin