S-Plastic Thermocomp QF002 is a compound based on Nylon 6/10 containing Glass Fiber.

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp QF002 resin is a compound based on Nylon 6/10 containing Glass Fiber.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	73	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	4600	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	121	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3960	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	80	MPa	ISO 527
Tensile Stress, break, 5 mm/min	76	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.3	%	ISO 527
Tensile Modulus, 1 mm/min	4580	MPa	ISO 527
Flexural Modulus, 2 mm/min	3760	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	325	J/m	ASTM D 4812
Izod Impact, notched, 23°C	36	J/m	ASTM D 256
Multiaxial Impact	1	J	ISO 6603
Instrumented Impact Total Energy, 23°C	4	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	20	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	217	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	196	°C	ASTM D 648
CTE, -30°C to 30°C, flow	5.4E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	9.6E-05	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	215	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	183	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.16	-	ASTM D 792
Density	1.15	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.26	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.3 - 0.6	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.6 - 0.9	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.35	%	ISO 62
Source GMD, last updated:2010/04/05