S-Plastic Thermocomp QF00A IS PA6.10, Glass Fiber, Property

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp QF00A resin is PA6.10, Glass Fiber,Property

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	181	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	181	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2.5	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D 638
Tensile Modulus, 50 mm/min	18680	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	280	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	285	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	11440	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	181	MPa	ISO 527
Tensile Stress, break, 5 mm/min	181	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.3	%	ISO 527
Tensile Strain, break, 5 mm/min	2.3	%	ISO 527
Tensile Modulus, 1 mm/min	15510	MPa	ISO 527
Flexural Modulus, 2 mm/min	12870	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1305	J/m	ASTM D 4812
Izod Impact, notched, 23°C	160	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	75	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	14	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	221	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	213	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.5E+00	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.83E+00	1/°C	ASTM E 831
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	220	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	205	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.6	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.21	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.18 - 0.2	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.5 - 1.5	%	ASTM D 955
Density	1.6	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.28	%	ISO 62
Source GMD, last updated:02/04/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.12 - 0.2	%
Melt Temperature	270 - 275	°C
Front - Zone 3 Temperature	270 - 280	°C
Middle - Zone 2 Temperature	260 - 270	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:02/04/2008