S-Plastic Thermocomp LX03447 is a compound based on Polyketone containing Proprietary Fillers.

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp LX03447 resin is a compound based on Polyketone containing Proprietary Fillers.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	248	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	28540	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	370	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	365	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	23700	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	246	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.5	%	ISO 527
Tensile Modulus, 1 mm/min	28350	MPa	ISO 527
Flexural Stress	360	MPa	ISO 178
Flexural Modulus, 2 mm/min	23800	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	771	J/m	ASTM D 4812
Izod Impact, notched, 23°C	70	J/m	ASTM D 256
Multiaxial Impact	3	J	ISO 6603
Instrumented Impact Total Energy, 23°C	7	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	45	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	337	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	325	°C	ASTM D 648
CTE, -30°C to 30°C, flow	9.E+00	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	3.89E+01	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	335	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	318	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.43	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.05	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.1 - 3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.7 - 0.9	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.07	%	ISO 62
Source GMD, last updated:2009/09/02

Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.1	%
Melt Temperature	380 - 390	°C
Front - Zone 3 Temperature	380 - 395	°C
Middle - Zone 2 Temperature	365 - 375	°C
Rear - Zone 1 Temperature	350 - 360	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:2009/09/02
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.