S-Plastic Thermocomp M10009A is a compound based on Polypropylene resin, containing Flame Retardant. Added features include

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp M10009A resin is a compound based on Polypropylene resin, containing Flame Retardant. Added features include : Flame

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 50 mm/min	38	MPa	ISO 527
Tensile Stress, break, 50 mm/min	25	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	7.3	%	ISO 527
Flexural Stress, yield, 2 mm/min	50	MPa	ISO 178
Flexural Modulus, 2 mm/min	1900	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	45	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	1.06E-04	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.4E-04	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	103	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	57	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow	1.6	%	S-Plastics Method
Density	1	g/cm³	ISO 1183
Water Absorption, 23°C/24hrs	0.01	%	ISO 62-1
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94V-2 Flame Class Rating (3)(4)	1.6	mm	UL 94 by GE
Source GMD, last updated:03/14/2008

Injection Molding	Value	Unit
Drying Temperature	70	°C
Drying Time	4	hrs
Melt Temperature	170 - 190	°C
Front - Zone 3 Temperature	180 - 190	°C
Middle - Zone 2 Temperature	170 - 180	°C
Rear - Zone 1 Temperature	160 - 170	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	25 - 50	rpm
Source GMD, last updated:03/14/2008
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.