S-Plastic Thermocomp UX06003 resin compound based on Polyphalamide resin containing Carbon Fiber. Added features include

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp UX06003 resin is a compound based on Polyphalamide resin containing Carbon Fiber. Added features include
Electrically Conductive, Mold Release, Heat Stabilized.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	275	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.8	%	ISO 527
Tensile Modulus, 1 mm/min	12600	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	353	MPa	ISO 178
Flexural Modulus, 2 mm/min	14500	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	40	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	7	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	1.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	6.3E-05	1/°C	ISO 11359-2
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow	0.1	%	S-Plastics Method
Density	1.28	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+04	Ohm	ASTM D 257
Source GMD, last updated:12/06/2007

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.15	%
Melt Temperature	315 - 330	°C
Front - Zone 3 Temperature	325 - 340	°C
Middle - Zone 2 Temperature	315 - 325	°C
Rear - Zone 1 Temperature	310 - 320	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:12/06/2007