S-Plastic Thermocomp AX06437 compound based on Acrylonitrile Butadiene Styrene resin containing Mineral.

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp AX06437 resin is a compound based on Acrylonitrile Butadiene Styrene resin containing Mineral.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	37	MPa	ASTM D 638
Tensile Stress, break	35	MPa	ASTM D 638
Tensile Stress, yld, Type I, 5 mm/min	37	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	34	MPa	ASTM D 638
Tensile Strain, yield	1.8	%	ASTM D 638
Tensile Strain, break	6	%	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.8	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	6.9	%	ASTM D 638
Tensile Modulus, 5 mm/min	3180	MPa	ASTM D 638
Flexural Stress	68	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	92	MPa	ASTM D 790
Flexural Modulus	3270	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3060	MPa	ASTM D 790
Tensile Stress, yield	36	MPa	ISO 527
Tensile Stress, break	33	MPa	ISO 527
Tensile Strain, break	7.5	%	ISO 527
Flexural Stress	64	MPa	ISO 178
Flexural Strain, break, 2 mm/min	64.1	%	ISO 178
Flexural Modulus	3010	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	288	J/m	ASTM D 4812
Izod Impact, notched, 23°C	26	J/m	ASTM D 256
Izod Impact, notched 80103 +23°C	3	kJ/m²	ISO 180/1A
Izod Impact, unnotched 80104 +23°C	22	kJ/m²	ISO 180/1U
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	86	°C	ASTM D 648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	87	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity, color	1.17	-	ASTM D 792
Density	1.175	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.22	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.5	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.6	%	ASTM D 955
Density	1.17	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.32	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Relative Permittivity, 1 GHz	2.75	-	ASTM D 150
Dissipation Factor, 1 GHz	0.0024	-	ASTM D 150
Source GMD, last updated:01/04/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.05 - 0.1	%
Melt Temperature	260	°C
Front - Zone 3 Temperature	265 - 275	°C
Middle - Zone 2 Temperature	230 - 245	°C
Rear - Zone 1 Temperature	205 - 215	°C
Mold Temperature	70 - 80	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:01/04/2008