S-Plastic Thermocomp DX07350 resin is a glass filled, Non-brominated & Non-chlorinated flame retardant polycarbonate. High s
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Thermocomp
Product Description
S-Plastics Thermocomp DX07350 resin is a glass filled, Non-brominated & Non-chlorinated flame retardant polycarbonate. High stiffness and good flow.
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 65 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 5 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4700 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 116 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4200 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 68 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 54 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 120 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4600 | MPa | ISO 178 |
| Pencil Hardness test, 0.5 kgf | F | - | ASTM D 3363 |
| Pencil Hardness test, 1kgf | HB | - | ASTM D 3363 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 35 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 11 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*3 +23°C | 50 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | 47 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 4 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | 75 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 61 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 112 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 102 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.7E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 3.7E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.6E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 109 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 112 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 104 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.29 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.35 - 0.45 | % | S-Plastics Method |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.09 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/2.16 kg | 21 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by GE |
| Source GMD, last updated:2008/06/27 | |||
Processing
Injection Molding Value Unit
Drying Temperature 80 - 90 °C
Drying Time 3 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 270 - 300 °C
Nozzle Temperature 270 - 290 °C
Front - Zone 3 Temperature 270 - 300 °C
Middle - Zone 2 Temperature 260 - 290 °C
Rear - Zone 1 Temperature 250 - 280 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 60 - 100 °C
Source GMD, last updated:2008/06/27
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
"(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294."
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin