S-Plastic Thermocomp EC008 is a compound based on Polyimide resin containing Carbon Fiber. Added features include: Elec
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Thermocomp
Product Description
S-Plastics Thermocomp EC008 resin is a compound based on Polyimide resin containing Carbon Fiber. Added features include: Electrically
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 211 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 27000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 286 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 22200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 214 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.44 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.E+03 | Ohm | ASTM D 257 |
Processing
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 360 - 365 | °C |
| Front - Zone 3 Temperature | 365 - 375 | °C |
| Middle - Zone 2 Temperature | 355 - 365 | °C |
| Rear - Zone 1 Temperature | 345 - 355 | °C |
| Mold Temperature | 120 - 150 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:2010/02/15 | ||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | ||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | ||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | ||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | ||
| (4) Internal measurements according to UL standards. | ||
| (5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. |
||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin