S-Plastics Thermocomp Noryl_FM3020 resin is GR/MR 30%, high modulus structural foam. 10% weight reduction, 0.250" wall thickness.

Property

MECHANICAL	Value	Unit	Standard
FOAM - MECHANICAL 6.4 mm Wt Reduction	10	%	-
Tensile Stress, yield, 6.35 mm	72	MPa	ASTM D 638
Tensile Strain, yield, 6.35 mm	2	%	ASTM D 638
Flexural Stress, yield, 6.4 mm	104	MPa	ASTM D 790
Flexural Modulus, 6.4 mm	6550	MPa	ASTM D 790
Hardness, Rockwell M	83	-	ASTM D 785
Taber Abrasion, CS-17, 1 kg	100	mg/1000cy	ASTM D 1044
Coefficient of Friction on self, Static	0.54	-	ASTM D 1894
Coefficient of Friction on steel, Static	0.51	-	ASTM D 1894
IMPACT	Value	Unit	Standard
FOAM - IMPACT 6.4 mm Wt Reduction	10	%	-
Izod Impact, notched, 23°C, 6.4mm	96	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
FOAM - THERMAL 6.4mm Wt Reduction	10	%	-
HDT, 0.45 MPa, 6.4 mm, unannealed	118	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	110	°C	ASTM D 648
CTE, -40°C to 95°C, flow	2.34E-05	1/°C	ASTM E 831
CTE, -40°C to 95°C, xflow	3.42E-05	1/°C	ASTM E 831
Relative Temp Index, Elec	50	°C	UL 746B
Relative Temp Index, Mech w/impact	50	°C	UL 746B
Relative Temp Index, Mech w/o impact	50	°C	UL 746B
PHYSICAL	Value	Unit	Standard
FOAM - PHYSICAL 6.4mm Wt Reduction	10	%	-
Weight Reduction	10	%	S-Plastics Method
Specific Gravity	1.32	-	ASTM D 792
Specific Gravity, foam molded	1.19	-	ASTM D 792
Water Absorption, 24 hours	0.08	%	ASTM D 570
Mold Shrinkage, flow, 6.4 mm	0.25	%	S-Plastics Method
Mold Shrinkage, xflow, 6.4 mm	0.3	%	S-Plastics Method
Poisson's Ratio	0.3	-	ASTM D 638
ELECTRICAL	Value	Unit	Standard
FOAM - ELECTRICAL 6.4 mm Wt Reduction	20	%	-
Volume Resistivity	1.E+17	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+17	Ohm	ASTM D 257
Arc Resistance, Tungsten {PLC}	6	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	0	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	4	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	4	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
FOAM - Flame Class Minimum Density	1.12	g/cm³	-
UL Recognized, 94V-1 Flame Class Rating (3)	2.89	mm	UL 94
UL Recognized, 94-5VA Rating (3)	2.89	mm	UL 94
Source GMD, last updated:12/04/1989

Processing

Parameter
Structural Foam Molding	Value	Unit
Blowing Agent, Physical System	Nitrogen Gas	-
Blowing Agent, Chemical System	FNC30X	-
Concentration Range (Blowing Agent)	1 - 3	%
Recommended Concentration (Blowing Agent)	2	%
Drying Temperature (Resin)	105 - 110	°C
Drying Time (Resin)	2 - 4	hrs
Drying Time (Resin, Cumulative)	8	hrs
Melt Temperature	270 - 310	°C
Nozzle Temperature	270 - 305	°C
Front Temperature	270 - 305	°C
Middle Temperature	270 - 305	°C
Rear Temperature	260 - 290	°C
Mold Temperature	65 - 80	°C
Source GMD, last updated:12/04/1989