S-Plastic Thermocomp Noryl_MX5819E resin NORYL MX5819E is a 20% carbon fibre reinforced, flame retarded PPO based injectio

Name: S-Plastic Thermocomp Noryl_MX5819E resin NORYL MX5819E is a 20% carbon fibre reinforced, flame retarded PPO based injectio
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp Noryl_MX5819E resin is NORYL MX5819E is a 20% carbon fibre reinforced, flame retarded PPO based injection moulding resin.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	95	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.5	%	ISO 527
Tensile Modulus, 1 mm/min	8500	MPa	ISO 527
Flexural Stress, break, 2 mm/min	130	MPa	ISO 178
Flexural Modulus, 2 mm/min	7500	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 80°C, flow	1.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	6.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/120	180	°C	ISO 306
PHYSICAL	Value	Unit	Standard
Density	1.18	g/cm³	ISO 1183
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-1 Flame Class Rating (3)	0.75	mm	UL 94
Source GMD, last updated:09/14/2000

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	2 - 4	hrs
Melt Temperature	290 - 330	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	310 - 330	°C
Middle - Zone 2 Temperature	290 - 310	°C
Rear - Zone 1 Temperature	270 - 290	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 120	°C
Source GMD, last updated:09/14/2000