S-Plastic Thermocomp DF004 compound based on Polycarbonate resin containing Glass Fiber.
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Thermocomp
Product Description
S-Plastics Thermocomp DF004 resin is a compound based on Polycarbonate resin containing Glass Fiber.
Property
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 91 | MPa | ASTM D 638 |
| Tensile Strain, break | 9.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5510 | MPa | ASTM D 638 |
| Flexural Stress | 68 | MPa | ASTM D 790 |
| Flexural Modulus | 5510 | MPa | ASTM D 790 |
| Tensile Stress, break | 102 | MPa | ISO 527 |
| Tensile Strain, break | 8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5940 | MPa | ISO 527 |
| Flexural Stress | 148 | MPa | ISO 178 |
| Flexural Modulus | 6000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 961 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 133 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 59 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 144 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 139 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.35 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.45 | % | ISO 294 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/24/2008 | |||
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin