S-Plastic Thermocomp PH0400CX_BK1D466 resin is 4.0 specific gravity, Nylon 6

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PH0400CX_BK1D466 resin is 4.0 specific gravity, Nylon 6

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	94	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	94	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.3	%	ASTM D 638
Tensile Modulus, 50 mm/min	17700	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	155	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	157	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	12900	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	92	MPa	ISO 527
Tensile Stress, break, 5 mm/min	92	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.4	%	ISO 527
Tensile Strain, break, 5 mm/min	1.5	%	ISO 527
Tensile Modulus, 1 mm/min	13980	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	153	MPa	ISO 178
Flexural Strain, break, 2 mm/min	1.6	%	ISO 178
Flexural Modulus, 2 mm/min	13260	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	431	J/m	ASTM D 4812
Izod Impact, notched, 23°C	71	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	14	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	27	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	7	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	195	°C	ASTM D 648
CTE, -30°C to 30°C, flow	2.61E+01	1/°C	ASTM E 831
CTE, -30°C to 30°C, xflow	4.01E+01	1/°C	ASTM E 831
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	197	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	4	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.17	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.44 - 0.46	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.81 - 0.83	%	ASTM D 955
Density	4	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.26	%	ISO 62
Source GMD, last updated:11/19/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 270	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	250 - 260	°C
Rear - Zone 1 Temperature	240 - 250	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:11/19/2008