S-Plastic Thermocomp WX09414_OR5E096 resin compound based on Thermoplastic Polyester (PBT) containing Glass. Characteris

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp WX09414_OR5E096 resin is a compound based on Thermoplastic Polyester (PBT) containing Glass. Characteristics ofthis grade are UL rated.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	88	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	87	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2.4	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	5930	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	134	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	127	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	5250	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	84	MPa	ISO 527
Tensile Stress, break, 5 mm/min	82	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.4	%	ISO 527
Tensile Strain, break, 5 mm/min	2.5	%	ISO 527
Tensile Modulus, 1 mm/min	5650	MPa	ISO 527
Flexural Stress	131	MPa	ISO 178
Flexural Modulus, 2 mm/min	5240	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	684	J/m	ASTM D 4812
Izod Impact, notched, 23°C	91	J/m	ASTM D 256
Multiaxial Impact	2	J	ISO 6603
Instrumented Impact Total Energy, 23°C	7	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	41	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	8	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	209	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	175	°C	ASTM D 648
CTE, -30°C to 30°C, flow	5.E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	1.16E-04	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	204	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	143	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.52	-	ASTM D 792
Density	1.51	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.06	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.7 - 0.9	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.8 - 1	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.08	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Comparative Tracking Index	150	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	1.5	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	2	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 2.0 mm	700	°C	IEC 60695-2-13
Oxygen Index (LOI)	30	%	ISO 4589
Source GMD, last updated:2010/08/16

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.05	%
Melt Temperature	240 - 265	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	245 - 255	°C
Rear - Zone 1 Temperature	220 - 230	°C
Mold Temperature	80 - 100	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2010/08/16