S-Plastic cycoloy C7122 mineral filled, non-halogenated flame retardant PC/ABS. Good stiffness with balanced flow and imp

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic cycoloy

Product Description

S-Plastics Cycoloy C7122 resin is a mineral filled, non-halogenated flame retardant PC/ABS. Good stiffness with balanced flow and impact performance.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	59	MPa	S-Plastics - Japan Method
Tensile Stress, yld, Type I, 5 mm/min	60	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	40	MPa	ASTM D 638
Tensile Strain, break	90	%	S-Plastics - Japan Method
Tensile Modulus, 5 mm/min	4230	MPa	ASTM D 638
Flexural Stress	95	MPa	ASTM D 790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	95	MPa	ASTM D 790
Flexural Modulus	3960	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3960	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	94	MPa	ISO 527
Tensile Strain, break, 5 mm/min	6.6	%	ISO 527
Tensile Modulus, 1 mm/min	4090	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	96	MPa	ISO 178
Flexural Modulus, 2 mm/min	4150	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	139	J/m	ASTM D 256
Izod Impact, notched, -30°C	57	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	65	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	8	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	6	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	8	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	91	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	85	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.1E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.9E-05	1/°C	ASTM E 831
CTE, -30°C to 30°C	5.E-05 - 7.E-05	1/°C	TMA
Vicat Softening Temp, Rate B/50	92	°C	ISO 306
Vicat Softening Temp, Rate B/120	93	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	83	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.28	-	ASTM D 792
Water Absorption, 24 hours	0.2	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm	0.3 - 0.4	%	S-Plastics Method
Melt Flow Rate, 260°C/2.16 kgf	13	g/10 min	ASTM D 1238
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-1 Flame Class Rating (3)	1.2	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating (3)	1.5	mm	UL 94
UL Recognized, 94-5VB Rating (3)	1.8	mm	UL 94
Source GMD, last updated:09/19/2002

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80 - 90	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	245 - 275	°C
Nozzle Temperature	245 - 275	°C
Front - Zone 3 Temperature	245 - 275	°C
Middle - Zone 2 Temperature	220 - 265	°C
Rear - Zone 1 Temperature	220 - 255	°C
Mold Temperature	60 - 80	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	30 - 80	%
Vent Depth	0.038 - 0.076	mm
Source GMD, last updated:09/19/2002