S-Plastic cycoloy CE1820 Cycoloy ABS + PC Blend, Low CTE, High Heat, High Impact,Extusion Thermoforming Grade

Name: S-Plastic cycoloy CE1820 Cycoloy ABS + PC Blend, Low CTE, High Heat, High Impact,Extusion Thermoforming Grade
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic cycoloy

Product Description

S-Plastics Cycoloy CE1820 resin is Cycoloy Extrusion Grade, ABS + PC Blend, Low CTE, High Heat, High Impact,Extusion Thermoforming Grade

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	56	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	60	MPa	ASTM D 638
Tensile Stress, yld, Type I, 5 mm/min	56	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	60	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	9	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	121	%	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	9	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	120	%	ASTM D 638
Tensile Modulus, 50 mm/min	3300	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	96	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2990	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	429	J/m	ASTM D 256
Izod Impact, notched, -30°C	108	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	57	J	ASTM D 3763
Instrumented Impact Energy @ peak, -30	51	J	ASTM D 3763
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	118	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	138	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D 648
CTE, -40°C to 40°C, xflow	8.1E-05	1/°C	ASTM E 831
CTE, -40°C to 60°C, flow	6.6E-05	1/°C	ASTM E 831
Thermal Conductivity	0.2	W/m-°C	ASTM C 177
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.22	-	ASTM D 792
Water Absorption, 24 hours	0.1	%	ASTM D 570
Water Absorption, equilibrium, 23C	0.4	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.6	%	S-Plastics Method
Melt Flow Rate, 230°C/3.8 kgf	1.5	g/10 min	ASTM D 1238
Melt Flow Rate, 260°C/5.0 kgf	11	g/10 min	ASTM D 1238
Source GMD, last updated:10/03/2003

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	90 - 100	°C
Drying Time	2 - 4	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	225 - 240	°C
Nozzle Temperature	220 - 230	°C
Front - Zone 3 Temperature	220 - 230	°C
Middle - Zone 2 Temperature	210 - 220	°C
Rear - Zone 1 Temperature	200 - 210	°C
Mold Temperature	70 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 80	%
Vent Depth	0.038 - 0.076	mm
Parameter
Sheet Extrusion	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	230 - 270	°C
Barrel - Zone 1 Temperature	215 - 255	°C
Barrel - Zone 2 Temperature	220 - 260	°C
Barrel - Zone 3 Temperature	225 - 270	°C
Adapter Temperature	240 - 270	°C
Die Temperature	240 - 270	°C
Roll Stack Temp - Top	70 - 95	°C
Roll Stack Temp - Middle	95 - 115	°C
Roll Stack Temp - Bottom	105 - 130	°C
Source GMD, last updated:10/03/2003