S-Plastic Valox VX4910 10% Glass Reinforced Nucleated PBT/ASA With Excellent Mechanical Properties High Dimensional

Name: S-Plastic Valox VX4910 10% Glass Reinforced Nucleated PBT/ASA With Excellent Mechanical Properties High Dimensional
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox VX4910 resin is 10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 5 mm/min	65	MPa	ISO 527
Tensile Stress, break, 5 mm/min	65	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	5	%	ISO 527
Tensile Strain, break, 5 mm/min	5	%	ISO 527
Tensile Modulus, 1 mm/min	4000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	100	MPa	ISO 178
Flexural Modulus, 2 mm/min	3750	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	5.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.2E-04	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	160	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.3	g/cm³	ISO 1183
Melt Volume Rate, MVR at 250°C/5.0 kg	20	cm³/10 min	ISO 1133
Source GMD, last updated:03/14/2008

Processing

Injection Molding	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 270	°C
Nozzle Temperature	240 - 260	°C
Front - Zone 3 Temperature	245 - 265	°C
Middle - Zone 2 Temperature	240 - 255	°C
Rear - Zone 1 Temperature	230 - 245	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	40 - 100	°C
Source GMD, last updated:03/14/2008