S-Plastics Valox X6600EX resin is Polyester+PC. High Heat. Excellent chemcial resistance.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	54	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	27	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	3.9	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	43	%	ASTM D 638
Tensile Modulus, 50 mm/min	2450	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	78	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2440	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	57	MPa	ISO 527
Tensile Stress, break, 50 mm/min	28	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4.1	%	ISO 527
Tensile Strain, break, 50 mm/min	27.7	%	ISO 527
Tensile Modulus, 1 mm/min	2490	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	80	MPa	ISO 178
Flexural Modulus, 2 mm/min	2300	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	59	J/m	ASTM D 256
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	85	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	77	°C	ASTM D 648
Vicat Softening Temp, Rate B/120	120	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	67	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.36	-	ASTM D 792
Melt Flow Rate, 266°C/5.0 kgf	24.1	g/10 min	ASTM D 1238
Density	1.36	g/cm³	ISO 1183
Melt Volume Rate, MVR at 265°C/2.16 kg	6	cm³/10 min	ISO 1133
Source GMD, last updated:06/15/2007

Parameter
Extrusion Blow Molding	Value	Unit
Drying Temperature	100 - 105	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	12	hrs
Maximum Moisture Content	0.01 - 0.03	%
Melt Temperature (Parison)	255 - 265	°C
Barrel - Zone 1 Temperature	250 - 260	°C
Barrel - Zone 2 Temperature	250 - 260	°C
Barrel - Zone 3 Temperature	255 - 260	°C
Barrel - Zone 4 Temperature	255 - 265	°C
Adapter - Zone 5 Temperature	255 - 265	°C
Head - Zone 6 - Top Temperature	255 - 265	°C
Head - Zone 7 - Middle Temperature	255 - 265	°C
Head - Zone 7 - Bottom Temperature	255 - 265	°C
Screw Speed	15 - 50	rpm
Extruder Feed Zone Temperature	255 - 265	°C
Accumulator Temperature	255 - 265	°C
Mold Temperature	50 - 95	°C
Die Temperature	255 - 265	°C
Source GMD, last updated:06/15/2007