S-Plastic Valox ENH4550 resin Is 25% GF Reinforced Non-Brominated & Non-Chlorinated Flame Retardant PBT Resin

Name: S-Plastic Valox ENH4550 resin Is 25% GF Reinforced Non-Brominated & Non-Chlorinated Flame Retardant PBT Resin
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox ENH4550resin is 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	115	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	115	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D 638
Tensile Modulus, 5 mm/min	11000	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	157	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	9370	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	115	MPa	ISO 527
Tensile Stress, break, 5 mm/min	115	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2	%	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	10400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	160	MPa	ISO 178
Flexural Modulus, 2 mm/min	9350	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	48	J/m	ASTM D 256
Izod Impact, notched, -30°C	42	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	6	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	38	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	34	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	5	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	5	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	205	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	205	°C	ASTM D 648
CTE, -40°C to 150°C, flow	2.2E+01	1/°C	ASTM E 831
CTE, -40°C to 150°C, xflow	7.7E+01	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	2.2E+01	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	9.1E+01	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	Pass	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	205	°C	ISO 306
Vicat Softening Temp, Rate B/120	205	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	205	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.52	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.9	%	S-Plastics Method
Melt Flow Rate, 250°C/5.0 kgf	24	g/10 min	ASTM D 1238
Density	1.52	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.25	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.07	%	ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg	18	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Hot Wire Ignition {PLC)	0	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	0	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
Comparative Tracking Index	300	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	0.75	mm	UL 94
UL Recognized, 94-5VA Rating (3)	3	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	0.75	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 0.8 mm	775	°C	IEC 60695-2-13
Source GMD, last updated:12/01/2008

Processing

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.