S-Plastic Valox EXVX0003 resin Is Will Be Commercialized As V8030RE. PRELIMINARY DATA15% GR, Post-Consumer Recycle

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox EXVX0003 resin is Will be commercialized as V8030RE. PRELIMINARY DATA. 15% GR, post-consumer recycle based, hydrostable PBT+PET. USCAR IIIcompliant. Automotive Spec for GM, Ford, Chrysler.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	82	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	82	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2.6	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.7	%	ASTM D 638
Tensile Modulus, 5 mm/min	5200	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	137	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	5100	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	325	J/m	ASTM D 4812
Izod Impact, notched, 23°C	42	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	5	J	ASTM D 3763
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	187	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	104	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow, 3.2 mm	0.6 - 0.8	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	0.7 - 0.9	%	S-Plastics Method
Source GMD, last updated:01/03/2002

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	60 - 75	°C
Drying Time	4 - 5	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.05	%
Minimum Moisture Content	0.02	%
Melt Temperature	255 - 275	°C
Nozzle Temperature	255 - 270	°C
Front - Zone 3 Temperature	255 - 265	°C
Middle - Zone 2 Temperature	250 - 260	°C
Rear - Zone 1 Temperature	245 - 255	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 80	rpm
Shot to Cylinder Size	30 - 80	%
Vent Depth	0.025 - 0.038	mm
Source GMD, last updated:01/03/2002

Other related products we recommend:

For more information please download the datasheet

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!