S-Plastic Lubricomp Noryl_NWR5810 LNP* Lubricomp* Noryl_NWR5810 compound is a 10% PTFE filled PPE+PS. High flow and good imp
resistance/lubricity. Electronics.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 39 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 37 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 2.8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2170 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 61 | MPa | ASTM D 790 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 57 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2060 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 1990 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 2242 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 232 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 32 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 110 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 113 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 97 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 116 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 105 | °C | ASTM D 648 |
| CTE, -40°C to 60°C, flow | 6.48E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 60°C, xflow | 7.38E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.11 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.55 - 0.7 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.45 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/5.0 kgf | 5.5 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:01/07/2000 | |||
Processing
| Parameter | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 95 - 100 | °C | |
| Drying Time | 3 - 4 | hrs | |
| Drying Time (Cumulative) | 8 | hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260 - 290 | °C | |
| Nozzle Temperature | 260 - 290 | °C | |
| Front - Zone 3 Temperature | 250 - 290 | °C | |
| Middle - Zone 2 Temperature | 240 - 280 | °C | |
| Rear - Zone 1 Temperature | 225 - 275 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Shot to Cylinder Size | 30 - 70 | % | |
| Vent Depth | 0.038 - 0.051 | mm | |
| Source GMD, last updated:01/07/2000 | |||
Our customers
In recent years, we have deeply cultivated the domestic market and actively explored foreign markets.Up to now, we have provided high-quality products and services to more than 1,000 customers in various industries, including: electronics and electrical appliances, medical, food, automotive electronics, optoelectronic communications, photovoltaic new energy, water treatment, transportation and other industries.
Samtion chemical supplies engineering plastics and special modified materials of S-Plastics and other brands.Our authentic products are guaranteed, with complete qualifications and superior supply capacity and price advantages.
Every batch of our products is subject to strict quality inspection to ensure the original supply. All products have MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA certificates!!
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Lubricomp Noryl_NWR5810.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.