S-Plastic Valox EXVX1189 Resin Is Glass Filled PBT Designed For High Strength Good Impact And Fatique Properties With Low

Name: S-Plastic Valox EXVX1189 Resin Is Glass Filled PBT Designed For High Strength Good Impact And Fatique Properties With Low
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox EXVX1189resin is Glass filled PBT designed for high strength, good impact and fatique properties with low plating-out during molding.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	122	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	122	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2.4	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D 638
Tensile Modulus, 5 mm/min	11520	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	195	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	9350	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	121	MPa	ISO 527
Tensile Stress, break, 5 mm/min	121	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.4	%	ISO 527
Tensile Strain, break, 5 mm/min	2.6	%	ISO 527
Tensile Modulus, 1 mm/min	10470	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	186	MPa	ISO 178
Flexural Modulus, 2 mm/min	8720	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	137	J/m	ASTM D 256
Izod Impact, notched, -30°C	81	J/m	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	n.m.	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	11	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	12	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	8	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	21	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	211	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	206	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.9E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	9.8E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/120	210	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	208	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.52	-	ASTM D 792
Melt Flow Rate, 250°C/2.16 kgf	11.4	g/10 min	ASTM D 1238
Density	1.52	g/cm³	ISO 1183
Melt Volume Rate, MVR at 250°C/2.16 kg	7	cm³/10 min	ISO 1133
Source GMD, last updated:05/11/2005

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	12	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 265	°C
Nozzle Temperature	245 - 260	°C
Front - Zone 3 Temperature	250 - 265	°C
Middle - Zone 2 Temperature	245 - 260	°C
Rear - Zone 1 Temperature	240 - 255	°C
Mold Temperature	65 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 80	rpm
Shot to Cylinder Size	40 - 80	%
Vent Depth	0.025 - 0.038	mm
Source GMD, last updated:05/11/2005