Product Description

S-Plastics Cycolac EX39P resin is High impact pipe extrusion ABS for drain, waste, and vent applications. Meets NSF/CSA cell class 42221

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	35	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	30	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	3.3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	90	%	ASTM D 638
Tensile Modulus, 5 mm/min	1730	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	59	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	1990	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	32	MPa	ISO 527
Tensile Stress, break, 50 mm/min	24	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.1	%	ISO 527
Tensile Strain, break, 50 mm/min	37.4	%	ISO 527
Flexural Stress, yield, 2 mm/min	46	MPa	ISO 178
Flexural Modulus, 2 mm/min	1460	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	459	J/m	ASTM D 256
Izod Impact, notched, -30°C	309	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	41	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	32	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	21	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	29	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	106	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	93	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	80	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.1E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.19E-04	1/°C	ASTM E 831
Vicat Softening Temp, Rate B/50	86	°C	ISO 306
Vicat Softening Temp, Rate B/120	89	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	74	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.03	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)	0.5 - 0.8	%	S-Plastics Method
Melt Flow Rate, 230°C/3.8 kgf	0.5	g/10 min	ASTM D 1238
Density	1.03	g/cm³	ISO 1183
Source GMD, last updated:2010/02/25

Processing

• Recommend initial lower temperatures settings to avoid material degradation/hang-up in die.
Parameter
Sheet Extrusion	Value	Unit
Drying Temperature	80 - 95	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	215 - 260	°C
Barrel - Zone 1 Temperature	170 - 200	°C
Barrel - Zone 2 Temperature	180 - 220	°C
Barrel - Zone 3 Temperature	190 - 225	°C
Barrel - Zone 4 Temperature	200 - 240	°C
Adapter Temperature	205 - 250	°C
Die Temperature	205 - 250	°C
Roll Stack Temp - Top	90 - 95	°C
Roll Stack Temp - Middle	95 - 105	°C
Roll Stack Temp - Bottom	100 - 105	°C
Source GMD, last updated:2010/02/25