S-Plastic Cycolac GDT5500L Low gloss, medium heat grade of ABS used for interior automotive components.
S-Plastics Cycolac GDT5500L resin is Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures,among others.
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 45 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 22 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 73 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2240 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 197 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 86 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 93 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.05 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.8 | % | S-Plastics Method |
| Melt Flow Rate, 230°C/5 kgf | 5 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:06/18/1999 | |||
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 10 | hrs |
| Melt Temperature | 250 - 280 | °C |
| Mold Temperature | 40 - 60 | °C |
| Source GMD, last updated:06/18/1999 | ||
Our warehouse
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
For more information please download the datasheet | |
 | |
Get The Latest Quotation |
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.