S-Plastic cycoloy EXCY0200 Bio Cycoloy with 50% content from renewable sources using proprietary copolymer

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic cycoloy

Product Description

S-Plastics Cycoloy EXCY0200 resin is Bio Cycoloy with 50% content from renewable sources using proprietary copolymer

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 50 mm/min	65	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	25	%	ISO 527
Tensile Modulus, 1 mm/min	2350	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	90	MPa	ISO 178
Flexural Modulus, 2 mm/min	2350	MPa	ISO 178
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/120	103	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	75	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.25	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	1.1	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg	19	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	>1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 0.8 mm	41	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm	28	kV/mm	IEC 60243-1
Dissipation Factor, 100 kHz	0.007	-	IEC 60250
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.5	mm	UL 94
UL Recognized, 94HB Flame Class Rating 2nd value (3)	3	mm	UL 94
Source GMD, last updated:10/15/2007

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	6	hrs
Extended Drying Temperature	60	°C
Extended Drying Time	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	230 - 260	°C
Nozzle Temperature	210 - 250	°C
Front - Zone 3 Temperature	220 - 260	°C
Middle - Zone 2 Temperature	220 - 260	°C
Rear - Zone 1 Temperature	200 - 230	°C
Hopper Temperature	50 - 70	°C
Mold Temperature	50 - 80	°C
Source GMD, last updated:10/15/2007