High Flow S-Plastic ABS Plastic Resin PC Cycoloy XCY480

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic cycoloy

Product Description

S-Plastics Cycoloy XCY480 resin is High flow

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	49	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	42	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	4	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	40	%	ASTM D 638
Tensile Modulus, 50 mm/min	2270	MPa	ASTM D 638
Tensile Modulus, 5 mm/min	2270	MPa	ASTM D 638
Flexural Stress	73	MPa	ASTM D 790
Flexural Modulus	2140	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	51	MPa	ISO 527
Tensile Stress, break, 50 mm/min	43	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4	%	ISO 527
Tensile Strain, break, 50 mm/min	50	%	ISO 527
Tensile Modulus, 1 mm/min	2150	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	47	MPa	ISO 178
Flexural Modulus, 2 mm/min	2100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	560	J/m	ASTM D 256
Izod Impact, notched, 0°C	450	J/m	ASTM D 256
Izod Impact, notched, -30°C	260	J/m	ASTM D 256
Multiaxial Impact	130	J	ISO 6603
Izod Impact, notched 80103 +23°C	55	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 0°C	46	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C	19	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	55	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	20	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	117	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	95	°C	ASTM D 648
CTE, -30°C to 80°C, flow	8.E-05	1/°C	ISO 11359-2
CTE, -30°C to 80°C, xflow	8.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	129	°C	ISO 306
Vicat Softening Temp, Rate B/50	118	°C	ISO 306
Vicat Softening Temp, Rate B/120	118	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	118	°C	ISO 75/Be
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	94	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	95	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow	0.5 - 0.7	%	S-Plastics Method
Melt Flow Rate, 260°C/5.0 kgf	35	g/10 min	ASTM D 1238
Density	1.13	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.47	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.14	%	ISO 62
Melt Volume Rate, MVR at 260°C/2.16 kg	12	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 260°C/5.0 kg	31	cm³/10 min	ISO 1133
Source GMD, last updated:04/02/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	90 - 100	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	240 - 270	°C
Nozzle Temperature	220 - 260	°C
Front - Zone 3 Temperature	230 - 270	°C
Middle - Zone 2 Temperature	230 - 270	°C
Rear - Zone 1 Temperature	210 - 240	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	60 - 90	°C
Source GMD, last updated:04/02/2008