S-Plastics Stat-kon DD0009PC resin is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features
of this material include: Electrically Conductive.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	61	MPa	ASTM D 638
Tensile Stress, break	53	MPa	ASTM D 638
Tensile Strain, yield	4.9	%	ASTM D 638
Tensile Strain, break	11	%	ASTM D 638
Tensile Modulus, 50 mm/min	2620	MPa	ASTM D 638
Flexural Stress	101	MPa	ASTM D 790
Flexural Modulus	2820	MPa	ASTM D 790
Tensile Stress, yield	59	MPa	ISO 527
Tensile Stress, break	51	MPa	ISO 527
Tensile Strain, yield	4.6	%	ISO 527
Tensile Strain, break	15.3	%	ISO 527
Tensile Modulus, 1 mm/min	2700	MPa	ISO 527
Flexural Stress	98	MPa	ISO 178
Flexural Modulus	2900	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	2531	J/m	ASTM D 4812
Izod Impact, notched, 23°C	119	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	15	J	ASTM D 3763
Multiaxial Impact	35	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	137	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	11	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	140	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	128	°C	ASTM D 648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	130	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.29	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.14	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.8	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.8	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.77	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.79	%	ISO 294
Moisture Absorption (23°C / 50% RH)	0.23	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
Source GMD, last updated:09/30/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/30/2004