S-Plastic Ultem DU329 WILL BE COMMERCIALIZED AS 6040 PRELIMINARY DATA PEI High Heat Stabilized Plateable

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Ultem

Product Description

S-Plastics Ultem DU329 resin is WILL BE COMMERCIALIZED AS 6040. PRELIMINARY DATA. PEI. High heat stabilized. Plateable. Automotive, connectors, food service.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	103	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	93	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	7	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	25.4	%	ASTM D 638
Tensile Modulus, 5 mm/min	3200	MPa	ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	158	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	3030	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	37	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	0	J	ASTM D 3763
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	218	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	212	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Melt Flow Rate, 337°C/6.6 kgf	50	g/10 min	ASTM D 1238
Source GMD, last updated:06/05/2000

Processing

Injection Molding	Value	Unit
Drying Temperature	150	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	24	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	365 - 390	°C
Nozzle Temperature	360 - 380	°C
Front - Zone 3 Temperature	365 - 390	°C
Middle - Zone 2 Temperature	355 - 375	°C
Rear - Zone 1 Temperature	345 - 365	°C
Mold Temperature	135 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:06/05/2000