S-Plastic Ultem EXUM0026 40% Milled Glass Filled High Flow Polyimide (Tg 217C) With Internal Mold Release

Name: S-Plastic Ultem EXUM0026 40% Milled Glass Filled High Flow Polyimide (Tg 217C) With Internal Mold Release
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Ultem

Product Description

S-Plastics Ultem EXUM0026 resin is 40% milled glass filled, high flow Polyimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming,UL94 V0 listing.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	115	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	115	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.5	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.5	%	ASTM D 638
Tensile Modulus, 5 mm/min	11000	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	159	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	6890	MPa	ASTM D 790
Taber Abrasion, CS-17, 1 kg	70	mg/1000cy	S-Plastics Method
Tensile Stress, yield, 5 mm/min	90	MPa	ISO 527
Tensile Stress, break, 5 mm/min	90	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2	%	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	11100	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	145	MPa	ISO 178
Flexural Stress, break, 2 mm/min	145	MPa	ISO 178
Flexural Modulus, 2 mm/min	7200	MPa	ISO 178
Hardness, H358/30	165	MPa	ISO 2039-1
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	443	J/m	ASTM D 4812
Izod Impact, notched, 23°C	54	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	25	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	25	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	222	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	219	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	210	°C	ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed	217	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	208	°C	ASTM D 648
CTE, -40°C to 150°C, flow	2.5E-05	1/°C	ASTM E 831
CTE, -40°C to 150°C, xflow	3.E-05	1/°C	ASTM E 831
Thermal Conductivity	0.28	W/m-°C	ISO 8302
CTE, 23°C to 150°C, flow	2.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	3.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	Passes	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	213	°C	ISO 306
Vicat Softening Temp, Rate B/120	214	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	207	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	200	°C	ISO 75/Ae
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	206	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	195	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.58	-	ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2)	0.2 - 0.4	%	S-Plastics Method
Mold Shrinkage, flow, 3.2 mm	0.2 - 0.4	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	0.3 - 0.5	%	S-Plastics Method
Melt Flow Rate, 337°C/6.6 kgf	9.5	g/10 min	ASTM D 1238
Density	1.58	g/cm³	ISO 1183
Melt Volume Rate, MVR at 360°C/5.0 kg	13	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Arc Resistance, Tungsten {PLC}	5	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	4	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	4	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	3	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	0.4	mm	UL 94
Source GMD, last updated:10/23/2003

Processing

Injection Molding	Value	Unit
Drying Temperature	150	°C
Drying Time	4 - 6	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	370 - 410	°C
Nozzle Temperature	370 - 410	°C
Front - Zone 3 Temperature	380 - 420	°C
Middle - Zone 2 Temperature	370 - 410	°C
Rear - Zone 1 Temperature	350 - 390	°C
Hopper Temperature	80 - 100	°C
Mold Temperature	140 - 180	°C
Source GMD, last updated:10/23/2003