S-Plastic Ultem EXUM0183 Developmental Glass Fiber And Mineral Filled PEI Resin Providing UL508 Compliance
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Ultem
Product Description
S-Plastics Ultem EXUM0183 resin is Developmental glass fiber and mineral filled PEI resin. Providing UL508 compliance through improved CTI. Providing excellent dimension stability and mechanical performance up to high temperatures.
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 0 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 126 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 15400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 192 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 13800 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 114 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 167 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 49 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 211 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/120 | 0 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.71 | - | ASTM D 792 |
| Melt Flow Rate, 200°C/3.8 kgf | 0 | g/10 min | ASTM D 1238 |
| Melt Flow Rate, 367°C/6.6 kgf | 6.5 | g/10 min | ASTM D 1238 |
| Density | 1.71 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 0 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/08/2007 | |||
Processing
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 360 - 390 | °C |
| Nozzle Temperature | 360 - 390 | °C |
| Front - Zone 3 Temperature | 360 - 390 | °C |
| Middle - Zone 2 Temperature | 360 - 380 | °C |
| Rear - Zone 1 Temperature | 340 - 380 | °C |
| Mold Temperature | 140 - 160 | °C |
| Back Pressure | 4.5 - 9.5 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Source GMD, last updated:08/08/2007 | ||
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin