S-Plastics Ultem SF2360 resin is High flow Ultem for thin wall application
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 148 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 11950 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 212 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9940 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 152 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Flexural Modulus, 2 mm/min | 9940 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 89 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 203 | °C | ASTM D 648 |
| CTE, -40°C to 150°C, flow | 1.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 150°C, xflow | 5.4E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C to 150°C, flow | 1.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 6.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 208 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.53 | - | ASTM D 792 |
| Moisture absorption (23°C/50%) | 0.04 | % | - |
| Mold Shrinkage, flow | 0.39 | % | S-Plastics Method |
| Mold Shrinkage, xflow | 0.47 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 18 | g/10 min | ASTM D 1238 |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.1 | % | ISO 62-1 |
| Melt Volume Rate, MVR at 345°C/10.0 kg | 40 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:05/23/2008 | |||
Processing
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 350 - 400 | °C |
| Nozzle Temperature | 345 - 400 | °C |
| Front - Zone 3 Temperature | 345 - 400 | °C |
| Middle - Zone 2 Temperature | 340 - 400 | °C |
| Rear - Zone 1 Temperature | 330 - 400 | °C |
| Mold Temperature | 135 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:05/23/2008 | ||
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin