S-Plastics Ultem SILTEM-STM1500 resin is a flexible siloxane-polyimide copolymer for cable and wire coatings. Non-halogenated and

Property

MECHANICAL	Value	Unit	Standard
Taber Abrasion, CS-17, 1 kg	60	mg/1000cy	S-Plastics Method
Tensile Stress, yield, 50 mm/min	20	MPa	ISO 527
Tensile Stress, break, 50 mm/min	25	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	15	%	ISO 527
Tensile Strain, break, 50 mm/min	110	%	ISO 527
Tensile Modulus, 1 mm/min	590	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	20	MPa	ISO 178
Flexural Stress, break, 2 mm/min	18	MPa	ISO 178
Flexural Modulus, 2 mm/min	470	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	25	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	15	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 80°C, flow	1.1E-04	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	9.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	75	°C	ISO 306
Vicat Softening Temp, Rate B/120	78	°C	ISO 306
PHYSICAL	Value	Unit	Standard
Mold Shrinkage on Tensile Bar, flow (2)	1.2 - 1.4	%	S-Plastics Method
Density	1.18	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.12	%	ISO 62
Melt Volume Rate, MVR at 320°C/2.16 kg	8	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	4.7E+14	Ohm-cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 3.2 mm	19	kV/mm	IEC 60243-1
Relative Permittivity, 100 Hz	3	-	IEC 60250
Dissipation Factor, 100 Hz	0.0091	-	IEC 60250
Comparative Tracking Index	175	V	IEC 60112
Comparative Tracking Index, M	100	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94V-1 Flame Class Rating (3)(4)	1.6	mm	UL 94 by GE
Glow Wire Flammability Index 960°C, passes at	3.2	mm	IEC 60695-2-12
Oxygen Index (LOI)	48	%	ISO 4589
Source GMD, last updated:03/26/1996

Processing

Profile Extrusion	Value	Unit
Drying Temperature	105 - 110	°C
Drying Time	5 - 7	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 320	°C
Barrel - Zone 1 Temperature	280 - 290	°C
Barrel - Zone 2 Temperature	300 - 310	°C
Barrel - Zone 3 Temperature	310 - 320	°C
Barrel - Zone 4 Temperature	310 - 325	°C
Hopper Temperature	60 - 100	°C
Adapter Temperature	315 - 325	°C
Die Temperature	300 - 320	°C
Calibrator Temperature	60 - 80	°C
Source GMD, last updated:03/26/1996