S-Plastic Ultem 6000 Transparent Standard Flow Polyimide Copolymer (Tg 235C) UL94 V0 Listing

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Ultem

Product Description

S-Plastics Ultem 6000 resin is Transparent, standard flow Polyimide copolymer (Tg 235C). ECO Conforming, UL94 V0 listing.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	113	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	113	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	7.5	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	17	%	ASTM D 638
Tensile Modulus, 5 mm/min	3510	MPa	ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	172	MPa	ASTM D 790
Flexural Stress, brk, 2.6 mm/min, 100 mm span	89	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	3580	MPa	ASTM D 790
Hardness, Rockwell M	110	-	ASTM D 785
Taber Abrasion, CS-17, 1 kg	8	mg/1000cy	ASTM D 1044
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1335	J/m	ASTM D 4812
Izod Impact, notched, 23°C	42	J/m	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	971	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	233	°C	ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed	221	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	211	°C	ASTM D 648
CTE, -20°C to 150°C, flow	5.22E-05	1/°C	ASTM E 831
CTE, -20°C to 150°C, xflow	5.4E-05	1/°C	ASTM E 831
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.29	-	ASTM D 792
Water Absorption, 24 hours	0.28	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	S-Plastics Method
Melt Flow Rate, 367°C/6.6 kgf	15.4	g/10 min	ASTM D 1238
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+17	Ohm-cm	ASTM D 257
Dielectric Strength, in oil, 1.6 mm	29.5	kV/mm	ASTM D 149
Relative Permittivity, 1 kHz	3	-	ASTM D 150
Dissipation Factor, 1 kHz	0.001	-	ASTM D 150
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	1.47	mm	UL 94
Oxygen Index (LOI)	44	%	ASTM D 2863
NBS Smoke Density, Flaming, Ds 4 min	5	-	ASTM E 662
Source GMD, last updated:01/13/2000

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	150	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	24	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	380 - 405	°C
Nozzle Temperature	375 - 400	°C
Front - Zone 3 Temperature	380 - 405	°C
Middle - Zone 2 Temperature	370 - 395	°C
Rear - Zone 1 Temperature	360 - 380	°C
Mold Temperature	135 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:01/13/2000