S-Plastic Ultem 9076 Standard Flow Polyimide Blend

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Ultem

Product Description

S-Plastics Ultem 9076 resin is Standard flow Polyimide Blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	96	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	92	%	ASTM D 638
Tensile Modulus, 5 mm/min	3300	MPa	ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	144	MPa	ASTM D 790
Flexural Stress, brk, 2.6 mm/min, 100 mm span	141	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	3240	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	74	J/m	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	2136	J/m	ASTM D 256
Gardner, 23°C	35	J	ASTM D 3029
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 6.4 mm, unannealed	188	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.3	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	0.5 - 0.7	%	S-Plastics Method
Melt Flow Rate, 295°C/6.6 kgf	1.4	g/10 min	ASTM D 1238
Halogen Content	0	%	S-Plastics Method
FLAME CHARACTERISTICS	Value	Unit	Standard
FAA Flammability, FAR 25.853 A/B	SECT A-1	-	FAR 25.853
OSU total heat release (2 minute test)	10	kW-min/m²	FAR 25.853
Vertical Burn a (60s) passes at	1	sec	FAR 25.853
Vertical Burn b (12s) passes at	0	sec	FAR 25.853
Source GMD, last updated:01/13/2000

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	135	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	10	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	350 - 370	°C
Nozzle Temperature	350 - 370	°C
Front - Zone 3 Temperature	350 - 370	°C
Middle - Zone 2 Temperature	345 - 365	°C
Rear - Zone 1 Temperature	340 - 360	°C
Mold Temperature	135 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:01/13/2000