Polyimide S-Plastic Ultem PEI Resin AUT195M OEM

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Ultem

Product Description

S-Plastics Ultem AUT195M resin is High flow Polyimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (S-Plastics test method). Contains low level of mold release.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	97	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	85	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	7	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	70	%	ASTM D 638
Tensile Modulus, 5 mm/min	3300	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	145	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3170	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	95	MPa	ISO 527
Tensile Stress, break, 50 mm/min	75	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6.5	%	ISO 527
Tensile Strain, break, 50 mm/min	20	%	ISO 527
Tensile Modulus, 1 mm/min	3000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	125	MPa	ISO 178
Flexural Modulus, 2 mm/min	3100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	2083	J/m	ASTM D 4812
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Izod Impact, notched, -30°C	55	J/m	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	2670	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	50	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	5	kJ/m²	ISO 180/1A
Charpy -30°C, V-notch Edgew 80103 sp=62mm	4	kJ/m²	ISO 179/1eA
Charpy 23°C, V-notch Edgew 80104 sp=62mm	4	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	209	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	187	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	191	°C	ASTM D 648
Thermal Conductivity	0.23	W/m-°C	ISO 8302
CTE, 23°C to 150°C, flow	5.E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	5.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	210	°C	ISO 306
Vicat Softening Temp, Rate B/50	200	°C	ISO 306
Vicat Softening Temp, Rate B/120	205	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	195	°C	ISO 75/Be
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	180	°C	ISO 75/Af
Metallized Haze Onset	195	°C	S-Plastics Method
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.26	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)	0.5 - 0.7	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm (5)	0.5 - 0.7	%	S-Plastics Method
Melt Flow Rate, 337°C/6.6 kgf	24	g/10 min	ASTM D 1238
Density	1.26	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.9	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.5	%	ISO 62
Melt Volume Rate, MVR at 340°C/5.0 kg	16	cm³/10 min	ISO 1133
Source GMD, last updated:2010/08/19

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	130 - 140	°C
Drying Time	3 - 4	hrs
Melt Temperature	340 - 380	°C
Nozzle Temperature	340 - 360	°C
Front - Zone 3 Temperature	340 - 360	°C
Middle - Zone 2 Temperature	330 - 350	°C
Rear - Zone 1 Temperature	320 - 340	°C
Hopper Temperature	80 - 100	°C
Mold Temperature	125 - 140	°C
Source GMD, last updated:2010/08/19