S-Plastic Stat-kon ZX08301 is a high heat compounds with ESD safe and low warpage performance suitable for use in Semicon

Name: S-Plastic Stat-kon ZX08301 is a high heat compounds with ESD safe and low warpage performance suitable for use in Semicon
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon ZX08301 resin is a high heat compounds with ESD safe and low warpage performance suitable for use in Semiconductor

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	120	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D 638
Tensile Modulus, 5 mm/min	11000	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	162	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	9000	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	46	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	200	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	194	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.4E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	5.6E-05	1/°C	ASTM E 831
PHYSICAL	Value	Unit	Standard
Density	1.29	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs (5)	0.2 - 0.35	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.3 - 0.45	%	ASTM D 955
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	5.5E+05 - 7.5E+05	Ohm-cm	ASTM D 257
Surface Resistivity	1.1E+05 - 2.5E+05	Ohm	ASTM D 257
Static Decay, 5000V to <50V	0.1	< seconds	FTMS101B
Source GMD, last updated:2009/08/18

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	105	°C
Drying Time	3 - 5	hrs
Melt Temperature	295 - 305	°C
Nozzle Temperature	290 - 295	°C
Front - Zone 3 Temperature	300 - 305	°C
Middle - Zone 2 Temperature	290 - 295	°C
Rear - Zone 1 Temperature	280 - 285	°C
Mold Temperature	90	°C
Back Pressure	9	MPa
Screw Speed	100	rpm