S-Plastic Stat-kon Noryl_FMC1010 a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL9

Name: S-Plastic Stat-kon Noryl_FMC1010 a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL9
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon Noryl_FMC1010 resin is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
FOAM - MECHANICAL 6.4 mm Wt Reduction	20	%	-
Tensile Stress, yield, 6.35 mm	45	MPa	ASTM D 638
Tensile Strain, break, 6.35 mm	4.1	%	ASTM D 638
Flexural Stress, yield, 6.4 mm	95	MPa	ASTM D 790
Flexural Modulus, 6.4 mm	5990	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
FOAM - IMPACT 6.4 mm Wt Reduction	20	%	-
Izod Impact, unnotched, 23°C, 6.4mm	154	J/m	ASTM D 4812
THERMAL	Value	Unit	Standard
FOAM - THERMAL 6.4mm Wt Reduction	20	%	-
HDT, 0.45 MPa, 6.4 mm, unannealed	103	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	97	°C	ASTM D 648
Relative Temp Index, Elec	50	°C	UL 746B
Relative Temp Index, Mech w/impact	50	°C	UL 746B
Relative Temp Index, Mech w/o impact	50	°C	UL 746B
PHYSICAL	Value	Unit	Standard
FOAM - PHYSICAL 6.4mm Wt Reduction	20	%	-
Specific Gravity	1.15	-	ASTM D 792
Specific Gravity, foam molded	0.92	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.15 - 0.25	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	0.2 - 0.4	%	S-Plastics Method
ELECTRICAL	Value	Unit	Standard
FOAM - ELECTRICAL 6.4 mm Wt Reduction	20	%	-
Volume Resistivity	8.E+03	Ohm-cm	ASTM D 257
Surface Resistivity	1.3E+04	Ohm	ASTM D 257
FLAME CHARACTERISTICS	Value	Unit	Standard
FOAM - Flame Class Minimum Density	0.96	g/cm³	-
UL Recognized, 94V-1 Flame Class Rating (3)	3.98	mm	UL 94
Source GMD, last updated:02/08/1993

Processing

Parameter
Structural Foam Molding	Value	Unit
Blowing Agent, Physical System	Nitrogen Gas	-
Blowing Agent, Chemical System	FNC30X	-
Concentration Range (Blowing Agent)	1 - 3	%
Recommended Concentration (Blowing Agent)	2	%
Drying Temperature (Resin)	105 - 110	°C
Drying Time (Resin)	2 - 4	hrs
Drying Time (Resin, Cumulative)	8	hrs
Melt Temperature	240 - 280	°C
Nozzle Temperature	265 - 280	°C
Front Temperature	260 - 280	°C
Middle Temperature	250 - 260	°C
Rear Temperature	240 - 250	°C
Mold Temperature	65 - 80	°C
Source GMD, last updated:02/08/1993