S-Plastic Stat-kon Noryl_HMC202M DATA ON BK1005 ONLY.

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon Noryl_HMC202M resin is DATA ON BK1005 ONLY.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	96	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	96	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	4.1	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	4.1	%	ASTM D 638
Tensile Modulus, 5 mm/min	7580	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	135	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	6890	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	86	MPa	ISO 527
Tensile Stress, break, 5 mm/min	86	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	145	MPa	ISO 178
Flexural Stress, break, 2 mm/min	145	MPa	ISO 178
Flexural Modulus, 2 mm/min	7150	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	267	J/m	ASTM D 4812
Izod Impact, notched, 23°C	42	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	9	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	180	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	177	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	171	°C	ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed	181	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	173	°C	ASTM D 648
CTE, -30°C to 30°C, flow	6.12E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	1.58E-04	1/°C	ASTM D 696
CTE, 23°C to 150°C, flow	1.3E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	5.7E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/120	180	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	177	°C	ISO 75/Af
Relative Temp Index, Elec	50	°C	UL 746B
Relative Temp Index, Mech w/impact	50	°C	UL 746B
Relative Temp Index, Mech w/o impact	50	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.18	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.1 - 0.3	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.6	%	S-Plastics Method
Melt Flow Rate, 300°C/5.0 kgf	7.6	g/10 min	ASTM D 1238
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+04	Ohm	ASTM D 257
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-1 Flame Class Rating (3)	1.49	mm	UL 94
Source GMD, last updated:12/14/2001

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	300 - 325	°C
Nozzle Temperature	300 - 325	°C
Front - Zone 3 Temperature	290 - 325	°C
Middle - Zone 2 Temperature	275 - 320	°C
Rear - Zone 1 Temperature	265 - 315	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 70	%
Source GMD, last updated:12/14/2001