S-Plastics Stat-kon EX99550C resin is a compound based on Polyimide resin containing Carbon Fiber. Added features of this material
include: Clean Compounding System.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	189	MPa	ASTM D 638
Tensile Strain, break	1.1	%	ASTM D 638
Tensile Modulus, 50 mm/min	20680	MPa	ASTM D 638
Flexural Stress	266	MPa	ASTM D 790
Flexural Modulus	18760	MPa	ASTM D 790
Tensile Stress, break	149	MPa	ISO 527
Tensile Strain, break	0.7	%	ISO 527
Tensile Modulus, 1 mm/min	22940	MPa	ISO 527
Flexural Stress	251	MPa	ISO 178
Flexural Modulus	18680	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	352	J/m	ASTM D 4812
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	8	J	ASTM D 3763
Multiaxial Impact	2	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	24	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	201	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.8E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	2.19E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.8E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	2.19E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	204	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.37	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.21	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.1	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.3	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.15	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.34	%	ISO 294
Moisture Absorption (23°C / 50% RH)	0.32	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+00 - 1.E+04	Ohm	ASTM D 257
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94V-0 Flame Class Rating (3)(4)	0.35	mm	UL 94 by GE
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.05	%
Melt Temperature	360 - 365	°C
Front - Zone 3 Temperature	365 - 375	°C
Middle - Zone 2 Temperature	355 - 365	°C
Rear - Zone 1 Temperature	345 - 355	°C
Mold Temperature	120 - 150	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:10/01/2004