S-Plastic Stat-kon FX98500 a compound based on Polyethylene resin containing Carbon Powder. Added features of this material

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon FX98500 resin is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	23	MPa	ASTM D 638
Tensile Stress, break	13	MPa	ASTM D 638
Tensile Strain, yield	15.8	%	ASTM D 638
Tensile Strain, break	43.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	1070	MPa	ASTM D 638
Flexural Stress	26	MPa	ASTM D 790
Flexural Modulus	870	MPa	ASTM D 790
Tensile Stress, yield	23	MPa	ISO 527
Tensile Stress, break	14	MPa	ISO 527
Tensile Strain, yield	14	%	ISO 527
Tensile Strain, break	82.8	%	ISO 527
Tensile Modulus, 1 mm/min	870	MPa	ISO 527
Flexural Stress	27	MPa	ISO 178
Flexural Modulus	930	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	No break	J/m	ASTM D 4812
Izod Impact, notched, 23°C	48	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	21	J	ASTM D 3763
Multiaxial Impact	63	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	46	°C	ASTM D 648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	48	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	0.976	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.02	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	2.7 - 3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.9 - 2.2	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	2.7 - 3	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.9 - 2.2	%	ISO 294
Density	0.97	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.02	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+02 - 1.E+05	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+02 - 1.E+05	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004