S-Plastic Stat-kon KX97157 a compound based on Acetal resin containing Carbon. Added features include : Electrically Conduct

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon KX97157 resin is a compound based on Acetal resin containing Carbon. Added features include : Electrically Conductive,
Impact Modified.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	84	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.7	%	ISO 527
Tensile Modulus, 1 mm/min	13100	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	96	MPa	ISO 178
Flexural Stress, break, 2 mm/min	89	MPa	ISO 178
Flexural Strain, break, 2 mm/min	1.7	%	ISO 178
Flexural Modulus, 2 mm/min	9600	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	3.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	9.8E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	152	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow	0.12	%	S-Plastics Method
Density	1.46	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+01 - 1.E+03	Ohm	ASTM D 257
Source GMD, last updated:03/10/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	200 - 215	°C
Front - Zone 3 Temperature	210 - 220	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:03/10/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon KX97157.pdf

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!