S-Plastic Stat-kon MD000 a compound based on Polypropylene resin containing Carbon Powder. Added features of this material i

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon MD000 resin is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material
include: Electrically Conductive.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	21	MPa	ASTM D 638
Tensile Stress, break	16	MPa	ASTM D 638
Tensile Strain, yield	8.4	%	ASTM D 638
Tensile Strain, break	47.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	1250	MPa	ASTM D 638
Flexural Stress	29	MPa	ASTM D 790
Flexural Modulus	1170	MPa	ASTM D 790
Tensile Stress, yield	21	MPa	ISO 527
Tensile Stress, break	15	MPa	ISO 527
Tensile Strain, yield	6.2	%	ISO 527
Tensile Strain, break	52	%	ISO 527
Tensile Modulus, 1 mm/min	1220	MPa	ISO 527
Flexural Stress	24	MPa	ISO 178
Flexural Modulus	1160	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D 4812
Izod Impact, notched, 23°C	817	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	33	J	ASTM D 3763
Multiaxial Impact	32	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	60	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	51	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.02E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.05E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.02E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.05E-04	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	53	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	0.95	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.03	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1.3 - 1.6	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.3 - 1.6	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.52	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.33	%	ISO 294
Density	0.95	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.03	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	225 - 250	°C
Front - Zone 3 Temperature	240 - 250	°C
Middle - Zone 2 Temperature	215 - 225	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/01/2004