S-Plastic Stat-kon PE002 a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include:

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon PE002 resin is a compound based on Nylon 6 resin containing Carbon Fiber. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	114	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	115	MPa	ASTM D 638
Tensile Strain, break	6.8	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	6.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	11720	MPa	ASTM D 638
Flexural Stress	172	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	179	MPa	ASTM D 790
Flexural Modulus	5510	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	5520	MPa	ASTM D 790
Tensile Stress, break	124	MPa	ISO 527
Tensile Stress, break, 5 mm/min	124	MPa	ISO 527
Tensile Strain, break	8	%	ISO 527
Tensile Strain, break, 5 mm/min	8.1	%	ISO 527
Tensile Modulus, 1 mm/min	8670	MPa	ISO 527
Flexural Stress	185	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	185	MPa	ISO 178
Flexural Modulus	7400	MPa	ISO 178
Flexural Modulus, 2 mm/min	7400	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	122	J/m	ASTM D 4812
Izod Impact, notched, 23°C	64	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	8	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	219	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	197	°C	ASTM D 648
CTE, -40°C to 40°C, flow	8.1E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	3.96E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	8.E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	3.9E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, flow	8.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	3.9E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	215	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	197	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.18	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	1	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.3 - 0.5	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.6 - 0.8	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.41	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.74	%	ISO 294
Density	1.18	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 275	°C
Front - Zone 3 Temperature	275 - 290	°C
Middle - Zone 2 Temperature	265 - 275	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008