S-Plastic Stat-kon PE002Z a compound based on Nylon 6 with Carbon Fiber. Characteristics: Extrusion Grade.

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon PE002Z resin is a compound based on Nylon 6 with Carbon Fiber. Characteristics: Extrusion Grade.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	58	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	32	%	ASTM D 638
Tensile Modulus, 50 mm/min	210	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	121	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	4070	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	59	MPa	ISO 527
Tensile Strain, break, 5 mm/min	10.8	%	ISO 527
Tensile Modulus, 1 mm/min	870	MPa	ISO 527
Flexural Stress	82	MPa	ISO 178
Flexural Modulus, 2 mm/min	2130	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1305	J/m	ASTM D 4812
Izod Impact, notched, 23°C	85	J/m	ASTM D 256
Multiaxial Impact	1	J	ISO 6603
Instrumented Impact Total Energy, 23°C	11	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	65	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	7	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	194	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	131	°C	ASTM D 648
CTE, -30°C to 30°C, flow	5.3E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	9.4E-05	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	195	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	134	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.18	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.93	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1 - 2	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.9	%	ASTM D 955
Density	1.18	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.93	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	7.E+00 - 9.E+00	Ohm	ASTM D 257
Source GMD, last updated:2009/01/13