S-Plastic Stat-kon QD000I a compound based on Nylon 6/10 resin containing Carbon Powder, Impact Modifier. Added features of

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Stat-kon

Product Description

S-Plastics Stat-kon QD000I resin is a compound based on Nylon 6/10 resin containing Carbon Powder, Impact Modifier. Added features of this
material include: Electrically Conductive, High Impact.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	31	MPa	ASTM D 638
Tensile Strain, break	52.7	%	ASTM D 638
Flexural Stress	54	MPa	ASTM D 790
Flexural Modulus	1720	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	603	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	55	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.17E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.17E-04	1/°C	ASTM E 831
PHYSICAL	Value	Unit	Standard
Density	1.11	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.28	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.2 - 0.4	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1 - 3	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1 - 3	%	ISO 294
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+02 - 1.E+04	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+02 - 1.E+04	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.12 - 0.2	%
Melt Temperature	270 - 275	°C
Front - Zone 3 Temperature	270 - 280	°C
Middle - Zone 2 Temperature	260 - 270	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/01/2004

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon QD000I.pdf

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!