Product Description

S-Plastics Stat-kon REL36 resin is PA 66, Carbon Fiber, PTFE,

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	154	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	154	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.1	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.1	%	ASTM D 638
Tensile Modulus, 50 mm/min	32440	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	302	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	16180	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	173	MPa	ISO 527
Tensile Stress, break, 5 mm/min	175	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.2	%	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	24610	MPa	ISO 527
Flexural Strain, break, 2 mm/min	181.7	%	ISO 178
Flexural Modulus, 2 mm/min	17350	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	569	J/m	ASTM D 4812
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Multiaxial Impact	3	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	41	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	261	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	253	°C	ASTM D 648
CTE, -40°C to 40°C, flow	8.E-01	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.87E+00	1/°C	ASTM E 831
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	261	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	252	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.394	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.52	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.15 - 0.17	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.8 - 0.1	%	ASTM D 955
Density	1.39	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.75	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	2.E+00 - 5.E+00	Ohm	ASTM D 257
Source GMD, last updated:02/04/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	275 - 290	°C
Front - Zone 3 Temperature	295 - 305	°C
Middle - Zone 2 Temperature	280 - 295	°C
Rear - Zone 1 Temperature	265 - 275	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:02/04/2008