S-Plastic Colorcomp M1000S Polypropylene Resin Pellets Unfilled Glow In The Dark

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Colorcomp

Product Description

S-Plastics Colorcomp M1000S resin is a compound based on Polypropylene resin containing Unfilled Glow In the Dark Custom Color. Added
features of this material include: Heat Stabilized.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	28	MPa	ISO 527
Tensile Stress, break	26	MPa	ISO 527
Tensile Strain, yield	7	%	ISO 527
Tensile Strain, break	40	%	ISO 527
Tensile Modulus, 1 mm/min	2160	MPa	ISO 527
Flexural Stress	40	MPa	ISO 178
Flexural Modulus	1800	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	130	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	94	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.13	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs	1.5 - 1.7	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.5 - 1.7	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.51 - 1.67	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.51 - 1.67	%	ISO 294
Density	1.12	g/cm³	ISO 1183
Source GMD, last updated:09/28/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	215 - 220	°C
Front - Zone 3 Temperature	205 - 215	°C
Middle - Zone 2 Temperature	200 - 210	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/28/2004

For more information please download the datesheet

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!