S-Plastic Geloy CR7010 ASA copolymer for sheet extrusion applications. High impact, weatherable capstock.

Name: S-Plastic Geloy CR7010 ASA copolymer for sheet extrusion applications. High impact, weatherable capstock.
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Geloy

Product Description

S-Plastics Geloy CR7010 resin is ASA copolymer for sheet extrusion applications. High impact, weatherable capstock.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	42	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	35	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	3.2	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	40	%	ASTM D 638
Tensile Modulus, 50 mm/min	1930	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	60	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	1930	MPa	ASTM D 790
Hardness, Rockwell R	91	-	ASTM D 785
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	480	J/m	ASTM D 256
Izod Impact, notched, -30°C	106	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	24	J	ASTM D 3763
Instrumented Impact Total Energy, -30°C	16	J	ASTM D 3763
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	102	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	90	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	76	°C	ASTM D 648
HDT, 1.82 MPa, annealed	97	°C	ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed	96	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	85	°C	ASTM D 648
CTE, -40°C to 40°C, flow	9.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.08E-04	1/°C	ASTM E 831
Relative Temp Index, Elec	50	°C	UL 746B
Relative Temp Index, Mech w/impact	50	°C	UL 746B
Relative Temp Index, Mech w/o impact	50	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.06	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.5	%	S-Plastics Method
Melt Flow Rate, 220°C/10.0 kgf	3.7	g/10 min	ASTM D 1238
Melt Flow Rate, 260°C/5.0 kgf	3.5	g/10 min	ASTM D 1238
OPTICAL	Value	Unit	Standard
Gloss, untextured, 60 degrees	95	-	ASTM D 523
ELECTRICAL	Value	Unit	Standard
Hot Wire Ignition {PLC)	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	0	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	0	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.49	mm	UL 94
UV-light, water exposure/immersion	F2	-	UL 746C
Source GMD, last updated:06/29/1998

Processing

• Barrel temperatures should be banked TO 150°C (300°F)
Parameter
Sheet Extrusion	Value	Unit
Drying Temperature	80 - 90	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	12	hrs
Minimum Moisture Content	0.04	%
Melt Temperature	220 - 245	°C
Barrel - Zone 1 Temperature	180 - 225	°C
Barrel - Zone 2 Temperature	190 - 230	°C
Barrel - Zone 3 Temperature	205 - 240	°C
Barrel - Zone 4 Temperature	210 - 245	°C
Adapter Temperature	210 - 245	°C
Die Temperature	210 - 245	°C
Roll Stack Temp - Top	70 - 100	°C
Roll Stack Temp - Middle	70 - 95	°C
Roll Stack Temp - Bottom	65 - 90	°C
Source GMD, last updated:06/29/1998