Modified S-Plastic PBT PC Plastic Injection Moulding Raw Materials Xenoy XD1647 Resin
S-Plastics Xenoy XD1647 resin is a semi crystalline, impact modified PBT+PC blend, containing 15% mineral filler. It is especially developed to obtain a reduced coefficient of thermal expansion combined with good chemical resistance. The material can be painted with water based and
solvent based paint systems.
Property
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 10 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3450 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 9 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, -30°C to 80°C, flow | 6.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 125 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 128 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 109 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.6 - 0.8 | % | S-Plastics Method |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 13 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:05/17/2001 | |||
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 270 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 240 - 265 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 80 | °C |
| Source GMD, last updated:05/17/2001 | ||
Our warehouse
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.