Unfilled PBT PC Blend S-Plastic Xenoy Resins Commodity XR100

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Xenoy

Product Description

S-Plastics Xenoy XR100 resin is ian unfilled PBT+PC blend containing post-industrial recycle, and is suitable for injection moulding applications which require ductility down to 0C.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3	%	ISO 527
Tensile Strain, break, 50 mm/min	20	%	ISO 527
Tensile Modulus, 1 mm/min	2000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	70	MPa	ISO 178
Flexural Modulus, 2 mm/min	2000	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	35	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 0°C	17	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -20°C	15	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 80°C, flow	1.1E-04	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	118	°C	ISO 306
Vicat Softening Temp, Rate B/120	120	°C	ISO 306
PHYSICAL	Value	Unit	Standard
Mold Shrinkage on Tensile Bar, flow (2) (5)	0.7 - 1	%	S-Plastics Method
Density	1.22	g/cm³	ISO 1183
Melt Volume Rate, MVR at 250°C/5.0 kg	17	cm³/10 min	ISO 1133
Source GMD, last updated:1993/09/14

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	90 - 100	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	255 - 270	°C
Nozzle Temperature	250 - 265	°C
Front - Zone 3 Temperature	250 - 270	°C
Middle - Zone 2 Temperature	240 - 265	°C
Rear - Zone 1 Temperature	230 - 250	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	60 - 80	°C
Source GMD, last updated:1993/09/14

For more information please download the datasheet

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!